English translation for "亚磷酸钠"
|
- sodium phosphite
Related Translations:
亚磷酸: orthopho horous acidorthophosphoric acidphosphonous acidphosphorousacid 亚磷酸铅: lead phosphite dibasic 原亚磷酸: ortho-phosphorous acid 亚磷酸钾: potassium phosphatepotassium phosphite 偏亚磷酸: metaphosphorous acid 亚磷酸氢钾: potassium hydrogen phosphite
- Example Sentences:
| 1. | With the increasing of knac4h4o6 * 4h2o and naacehso ? ? 2h2o , the speed of plating was increasing when the concentration of them was low
镀液的ph值与次亚磷酸钠和硫酸钴的摩尔比对镀层成分、及相结构的影响较为显著。 | | 2. | When the bath temperature is 90 and nah2po2 h2o concentration is more than 80g / l , wetting time prolongs instead and solderability decreases
镀液温度为90oc时，次亚磷酸钠用量超过809几后，润湿i时间反而增长，可焊性下降。 | | 3. | When the bath temperature is at 70 and 801 : , wetting time of the deposits shortened as the nah2po2 h2o concentration increases , and solderability improves
镀液温度在70t和80 ’ c时，镀层润湿时间随次亚磷酸钠浓度的增加而缩短，可焊性提高。 | | 4. | The experiments showed that these factors could increase the plating rate which the concentration of nah2 ? o2 " t ^ o , the ph and the temperature of electroless plating had been risen
实验表明：镀液ph值和施镀温度升高，次亚磷酸钠和缓冲剂浓度增加，镀速提高。 | | 5. | If phosphorus was adequacy in composite powder , co - p alloy coating becomes non - crystalline . the quality of composite powder was better , and the stabilization of solution is improved with the increase of the ph from 9 . 5 to 11 . 0
硫酸钴浓度18 40g / l ，次亚磷酸钠浓度20 40g / l ，可以得到镀覆均匀、分散性好的复合粉末；增加其浓度，复合粉体的镀覆质量得以提高。 | | 6. | " induction period " was reflected the quality of electroless plating solution , and affected the efficiency of electroless plating , " induction period " was shortened with the increase of the concentration of nah2 ? o2 ? i - ho and coso4 . it was shortened by increasing the ph and the loading of powder
硫酸钴和次亚磷酸钠浓度的增加，镀液的ph值升高，装载量的增大，反应的孕育期变短；镀速是反应时间与增重综合作用的结果。 | | 7. | On the basis of electroplating and immersion plating tin , and through large numbers of experiments , a new process of electroless plating tin in acid chloride bath solutions including sncl2 2h2o , nah2po2 h2o , special complexing agent , additive agent , stabilizing agent and antioxidant , was established . continuous self - catalyzed deposition of tin on copper substrate was achieved successfully , and half - bright and silvery - white tin deposits with excellent properties were obtained
本文是在电镀锡、浸镀锡工艺配方的基础上，通过大量的试验，确立了一种以氯化亚锡、次亚磷酸钠和特定的络合剂、添加剂、稳定剂，抗氧化剂为基本镀液组成的酸性氯化物化学镀锡体系，成功地在铜上实现了锡的连续自催化沉积，获得了性能优异的半光亮银白色锡镀层。 |
- Similar Words：
- "亚磷酸二月桂酯" English translation, "亚磷酸二正丁酯" English translation, "亚磷酸芳・烷基酯" English translation, "亚磷酸钾" English translation, "亚磷酸木溜油" English translation, "亚磷酸铅" English translation, "亚磷酸氢钡" English translation, "亚磷酸氢钙" English translation, "亚磷酸氢钾" English translation, "亚磷酸氢铅" English translation
|
|
|