| 1. | Surface modification of mg - based alloys by high current pulsed electron beam irradiation
镁合金强流脉冲电子束表面改性 |
| 2. | Calculation of protection dose at the labyrinthine outlet of electron beam irradiation apparatus
电子束辐照装置迷路出口处的防护剂量计算 |
| 3. | Besides , no distinct difference of the response between 60co y - ray irradiation and electron beam irradiation is found , nor energy and dose rate reliability
此外，在本实验范围内未发现丙氨酸薄膜剂量计对射线和电子束的响应存在明显的差异，同时未发现明显的能量和剂量率依赖性。 |
| 4. | In the linear dose range , the extensive uncertainty of alanine / esr dosimetry system is 4 % for 60co y - ray irradiation and 6 % for electron beam irradiation ( in 95 % confidence level )
在线性剂量范围内，该剂量体系测量60co射线和电子束吸收剂量的扩展不确定度分别为4 . 2和6 . 2 ( 95置信水平) ，适合作为电子束传递剂量标准。 |
| 5. | 3 . polycrystalline lif thin films were grown by thermal evaporation on amorphous substrates . properties of broad band photo - luminescence at room temperature of active channel ( f2 and fa + ) produced by electron beam irradiation were studied
首次用热蒸发法在玻璃衬底上制备了多晶lif薄膜平面波导，研究了由电子束照射产生的有源( f _ 2和f _ 3 ~ +色心)沟道的室温宽带光致发光特性。 |
| 6. | The agreement is also within the uncertainty when being compared with the alanine and cta film dosimeters made by jaeri . in addition , this dosimetry system is used to measure field and depth - dose distribution curves for 12mev electron beams , which shows it ' s suitability and practicability for electron beam irradiation
另外，还利用该剂量体系对12mev电子束辐照场的分布及深度剂量分布进行了实际测量，得到了与cta和fwt60等薄膜剂量计相一致的结果，这也进一步说明该剂量体系在电子束辐照上的适用性和实用性。 |
| 7. | By means of electron beam irradiation , some oxygen containing groupe are introduced on the molecular chain of lldpe , the interface compatibility of the composite is improved . the yield strength and young ' s modulus of ramie / lldpe are increased from 9 . 78 mpa , 432 mpa to 13 . 1 mpa and 633 mpa respectively
经电子束辐照后， lldpe分子链中引入含氧基团，苎麻电子束辐照lldpe复合材料的界面相容性提高，复合材料的屈服强度、杨氏模量从9 . 78mpa 、 432mpa提高到13 . 1mpa 、 633mpa 。 |