Chinese translation for "zinc electrode"
|
- 锌电极
锌电级
Related Translations:
- Example Sentences:
| 1. | At present , the main way to solve the problems is to add mercury and its oxide to zinc electrode
目前，主要解决问题的方法是在电极中加入汞及其氧化物。 | | 2. | As the material of batteries , zinc electrode has many problems , such as dendrite growth , shape - changing , passivation , corrosion and so on
但是，锌作为电极材料使用仍然存在问题，表现为：锌枝晶、形变、钝化和腐蚀。 | | 3. | Then , the preparation and electrochemical behavior of pasted zinc electrode and its application in the zn / ni battery were studied systematically in this paper
在此基础上，本文对锌电极的制备及电化学性能、以及在锌镍电池中的应用作了较系统的研究。 | | 4. | The addition of calcium hydroxide in zinc electrode can reduce the solubility of zinc oxide and improve discharge capacity , cycling life and utilization of active material
在氧化锌中加入氢氧化钙能显著降低氧化锌在碱性溶液中的溶解度，明显改善锌电极的放电容量、循环寿命以及活性物质的利用率。 | | 5. | As a part of zinc air battery , air electrode has become the key factor to the character of zinc - air battery , because of the stagnancy of the zinc electrode which is the anode electrode in the battery
空气电极作为锌空气电池中的一部分,在锌电极的研究几乎进入停滞阶段的现在,现已成为决定整个锌空气电池性能的关键。 | | 6. | By means of the electrochemical measurement , the effect of the metal oxide additives such as pbo , bi2o3 , in2o3 and electrolytic additive of : c16h33 ( ch3 ) 3nbr . on the performance of zinc electrode were investigated
电极添加剂主要考察了pbo 、 bi _ 2o _ 3 、 in _ 2o _ 3三种金属氧化物对锌电极性能的影响，电解液添加剂主要考察了十六烷基三甲基溴化铵的添加对锌电极性能的影响。 | | 7. | The research and development of chemical power sources , zinc - based and nickel - zinc batteries was reviewed . the shape change , dendrite formation , corrosion and passivation of the rechargeable zinc electrode and the ways to solve the above problems were discussed as well
本文全面概述了化学电源的发展，锌基电池的现状以及锌镍电池的发展状况，分析了可充锌电极存在的变形、枝晶、腐蚀与钝化的原因及其解决途径。 | | 8. | For the other hand , la2o3 additives can improve the activation process and discharge capacity obviously for zinc electrode . the appropriate content of la2o3 additives in zinc electrode can increase the electrochemical properties of the zinc electrode . zn / ni battery with the zinc electrode containing calcium additive showed better discharge capacity and charge - discharge cycling life
以锌酸钙为活性物质的锌电极能得到更高的锌利用率，且以锌酸钙为活性物质的锌镍电池的循环寿命明显优于以氧化锌为活性物质的锌镍电池；两层隔膜的锌镍电池的放电容量高于一层隔膜的锌镍电池，容量衰减速度也明显小于后者。 | | 9. | The result shows that the addition of pbo , bi2o3 , in2o3 in zinc electrode can improve the morphology of zinc deposition and prevent it from dendrite growth and deformation . and also , the dendrite growth of zinc was inhibited by the addition of c16 ( ch3 ) 3nbr in the electrolytes through the absorption in active sites on the surface of zinc electrode which will suppress zinc deposition
实验结果表明：在电极中适量添加pbo 、 bi _ 2o _ 3 、 in _ 2o _ 3三种金属氧化物可以明显改善锌沉积形态、抑制锌枝晶和变形；十六烷基三甲基溴化铵通过在锌电极表面的活性中心上特性吸附，抑制锌在这些位置的沉积，产生较均匀的沉积，从而达到抑制枝晶的效果。 | | 10. | Zinc acts as negative material of zinc manganese dioxide batteries , with the advantages of low cost , little poison and easy treatment . in another way , as the material of batteries , zinc electrode has many problems , such as dendrite growth , shape - changing , passivation , corrosion and so on . at present , the main way to solve these problems is to add mercury and its oxide to zinc electrode
锌锰电池采用锌粉作为电池的负极材料，锌资源丰富、价格低廉、毒性小、易处理，但是锌作为电极材料使用存在枝晶、形变、钝化和腐蚀等问题，目前，解决这些问题的主要方法是加入汞及其氧化物。 |
- Similar Words：
- "zinc dust precipitation" Chinese translation, "zinc dust primer" Chinese translation, "zinc dust process" Chinese translation, "zinc dust purification" Chinese translation, "zinc dusting powder" Chinese translation, "zinc electrolyte" Chinese translation, "zinc electrolyzing plant" Chinese translation, "zinc electroplating" Chinese translation, "zinc elimination" Chinese translation, "zinc engraving machine" Chinese translation
|
|
|