The weight loss temperature at 5wt % of bulk p ( mma - chmi ) / ommt2 was improved by about 100 contrast with that of pmma and mechanics properties were improved partly under the condition that the transparency was not decreased greatly indicated by and organic mmt ( ommt ) dispersed in the polymeric matrix evenly as nanostructure 结果表明：在基本不影响材料的透光率的前提下，本体法p ( mma ? chmi ) ommt2的5wt热失重温度比pmma提高100左右，其维卡软化温度提高4 ? 7 ，而且其拉伸等力学性能有不同程度的提高。