Home > chinese-english > "未熔合" in English

English translation for "未熔合"

lack of fusion/ incomplete fusion
non-fusion


Related Translations:
熔合:  fuse; mix together; merge; alloy
不熔合:  fritlessunfuse
熔合线:  bond weldfusion /bond linefusion boundaryfusion linefusion-lineline of fusionline of weldingmelt runweld bondweld junctionweldjunction
熔合原子:  united atom
热核熔合:  thermonuclear fusion
熔合接触:  bonded contactwelded contact
欠熔合:  lack of fusion
熔合过程:  alloying process
熔合宝石:  reconstructed stone
熔合能:  fusion energy
Example Sentences:
1.Furthermo re , the zinc vaporating and oxydizing cause air bubble , incomplete fusion and cr ack
锌挥发和氧化会导致气孔、未熔合及裂纹。
2.Internal defects : lack of penetration , lack of fusion , slag , gas pole , carck , overheating
内部缺陷:未焊透、未熔合、夹渣、气孔、裂纹、过热。
3.The microstructure of coat do not take place obvious change as increased induction current and decreased melt time
重熔层组织致密,未发现未熔合及夹渣等冶金缺陷。
4.According to the reasons of the flaw , find out the solutions and improve the welding quality of fibrin root welding
根据缺陷产生的原因,找出了解决这种特殊的根部未熔合缺陷产生的方法,提高了纤维素根焊的焊接质量。
5.It has mang virtues such as weld moulding beauty , weld quanlity credibility and so on , espcially it can conquer not weld fully , not fusion and so forth fatal vice
它具有焊缝成型美观、焊接质量可靠等优点,特别是对克服常规焊接方法中的未焊透、未熔合等危险性缺陷具有重要意义。
6.When doing a grooving and hammer breaking experiment on a sample in the technology assess teal of fibrin root welding , find that fibrin backing weld will easily produce a special root incomplete fusion flaw
摘要在进行一次纤维素根焊的工艺评定试验的过程中,对取样进行刻槽锤断实验时,发现采用纤维素打底焊容易产生一种特殊的根部未熔合缺陷。
Similar Words:
"未妊母猪" English translation, "未日浩劫" English translation, "未日救未来" English translation, "未融化的粒雪" English translation, "未熔穿" English translation, "未熔合点焊接头" English translation, "未熔化的" English translation, "未熔解的矿砂" English translation, "未熔解的炉渣" English translation, "未熔炉料" English translation