English translation for "焙烧时间"

roasting time

Related Translations:
焙烧:  roast; bake; torrefy; calcination; torrefaction◇焙烧料 calcines; 焙烧炉 roaster; roasting furnace; 焙烧窑 burning-in kiln
完全焙烧:  complete roastingdead roastingultimate roasting
焙烧强度:  fired strengthintensity of roasting
焙烧条件:  firing condition
脱硫焙烧:  desulphurizing roasting
炉渣焙烧:  slag roasting
焙烧鼓风炉:  roasting blast furnaceroasting blastfurnace
焙烧不足:  insufficient firingunderroasting
焙烧窑:  burning kilnburning-in kilncalcinercalcining kilnroasting kilnstack kiln
烧结焙烧:  agglomeration roastingsinter returns roastingsinter roasting
Example Sentences:
1.It ' s obtained that ph = 6 . 5 is a suited ph value for getting ideal product with good properties . the calcinate temperature is the key factors to transform the precursor to a pure product with spinel structure
研究了不同的工艺条件如溶液ph值、焙烧温度、焙烧时间、焙烧方式、 li / mn的比值对产物结构的影响。
2.Spinel limn2o4 begin to form at 350 with the sintering time of 4 hours because there are one li + and two mn2 + in one precursor molecule . when the sintering temperature is larger than 750 , a specific sintering route is designed to avoid the formation of li2mno3 impurities
前驱体的焙烧温度和焙烧时间对limn _ 2o _ 4样品的晶相结构有很大的影响,焙烧温度高于750时,应采用分段焙烧工艺以防止局部高温形成li _ 2mno _ 3杂质。
3.Through the synthesis of licoo2 by using non - water dispersant and two - step roasting , influences of microstructures of precursor , the roasting temperature and the reaction time on the electrochemical properties of licoo2 were studied . it indicated that co3o4 with nano - crystalline have very good electrochemical property , and can shorten solid reaction time
02的制备工艺,考察了不同微结构的co30 ;先驱物,焙烧温度和焙烧时间等工艺条件对licoo ,电化学性能的影响,其中以纳米晶co3o ;制备出的licooz表现出优良电化学性能,且大大缩短了反应时间。
4.The characteristic of different products at different calcinating temperatures and time , ph value of solution , raw materials were investigated . the results show that perfect spinel li4mn5o12 crystals whose size belongs to nanometer can be obtained from the precursor of lithium manganese oxides after being calcinated . it is founded that calcinating temperature has great influence on the crystal structure of li4mn5o12 and the optimized temperature is 500
结果表明焙烧温度是影响产物结构性能的最重要的因素,最佳焙烧温度为500 ,温度小于200不能形成完整的尖晶石结构,而焙烧温度超过500产物会发生分解;综合考虑焙烧时间最佳为8小时;溶液ph值也是影响产物性能的因素之一,实验证明前驱体合成ph = 9 . 0最佳;另外不同的原料也会影响产物的结构,考察了不同锂源的影响,选择li _ 2co _ 3为最佳锂源。
5.( 2 ) the affecting factors such as components in precipitation process , the add - on , add on of precipitator , calination temperature and calination time were studied in the preparation process of ceo2 nanoparticles . the tg was used to analyze the processor , the xrd , sem and tem were used to characterize the size of crystal type of products . by a series of designed experiments the interaction between different factors and impacts on the preparation of ceo2 nanoparticles were probed , and the optimum preparation condition was gotten
( 2 )对纳米二氧化铈制备过程中可能的一些影响因素(反应组分的浓度,沉淀剂的加入量,焙烧温度,焙烧时间等)进行了研究,并通过tg ? dta分析手段对前驱物进行热重分析;用xrd 、 sem及tem等测试手段对产物的粒度和晶型进行分析;探索了各个因素对纳米二氧化铈制备的影响及各因素间的交互作用;确定了在该试验条件下制备纳米二氧化铈比较优化的制备条件。