English translation for "电弧熔炼"

arc-melting
electric arc melting


Related Translations:
区域熔炼器:  zone refiner
电弧:  arc; electric arc; voltaic arc
电弧熔化炉:  arc-melting furnaceelectrometal furnace
电弧漂移:  wandering of an arc
电弧破碎:  electric arc shattering
焊接电弧:  welding arc
电弧喷枪:  arc pistol
脉动电弧:  pulsating arc
间接电弧:  indirect arc
电弧喷涂:  electric arc spraying
Example Sentences:
1.The results indicate that the microstructure of the as - cast nb - losi ( at . % )
结果表明,电弧熔炼法制备的铸态nb上( at
2.The foundation to develop nb - si system intermetallics base high temperature structure materials has also been established in some degree in this paper . arc melting , powder metallurgy and optical floating zone technology have been used and compared to fabricate the nb - si system intermetallics
运用电弧熔炼、粉末冶金热压烧结、粉末冶金冷等静压和光学悬浮单晶生长技术等方法制备了nb - si系金属间化合物,并对这四种方法制备的nb - si系金属间化合物进行了比较。
3.The results indicate that arc melting is a good method to produce nb - si system intermetallics due to its simpler technics , lower cost and compact products . however , powder metallurgy is found to be not suitable to produce the nb - si system intermetallics due to its coarse and loose products resulting from the poor molding property of nb and si mixed powders . optical floating zone technology , which is used to fabricate nb - si intermetallic composites for the first time , is also found to be a good way to produce nb - si system intermetallics because of its compact products and good property despite of its relatively high cost
结果表明,电弧熔炼方法制备得到的nb - si系金属间化合物比较致密,且制备工艺简单,经济实用,是一种合适的nb - si系金属间化合物制备方法;由于nb 、 si元素粉末的成型性很差,用粉末冶金方法(热压烧结和冷等静压)制备的nb - si系金属间化合物表面粗糙、致密度低,且成本较高,不宜用于制备nb - si系金属间化合物;首次用光学悬浮单晶生长技术制备的nb - si系金属间化合物复合材料致密度很高,尽管成本稍高,但由于性能最佳,也是一种合适的nb - si系金属间化合物制备方法。
4.The results reveal that the microstructure of the nb - si system intermetallics consists of nb and nbasi phases . because of unstable microstructure of nfysi phase at high temperature , the equilibrium nb + nbssia dual - phase microstructure of the nb - si system intermetallics should be acquired by means of heat - treatment
研究表明,采用电弧熔炼和单晶生长技术制备的nb - si系金属间化合物的显微组织主要由nb + nb _ 3si组成,而由于nb _ 3si相在高温下是不稳定的,为了得到稳定的nb + nb _ 5si _ 3双相组织,必须对材料进行热处理。
Similar Words:
"电弧熔化用金属粉末" English translation, "电弧熔接" English translation, "电弧熔接,电焊" English translation, "电弧熔接,弧焊" English translation, "电弧熔接接头机" English translation, "电弧熔炼法" English translation, "电弧熔炼海绵金属" English translation, "电弧熔炼晶棒" English translation, "电弧熔炼炉" English translation, "电弧熔炼钨" English translation