English translation for "限制膨胀"
|
- arrest inflation
confined expansion
Related Translations:
膨胀力: bulging forceexpansibilityexpansion powerexpansive forceexpansive powerswelling forcetension 膨胀压: dilation pressureoncotic pressureswelling pressure 烧结膨胀: clinkering expansionsintering swell 膨胀波: dilatation wavedilatational wavedilatationalwavedilational waveexpansion shockexpansion waveextensional waverarefaction wavewave of dilatation 土壤膨胀: soil swellingsoilswellingswelling of soil
- Example Sentences:
| 1. | Standard test method for restrained expansion of expansive cement mortar
膨胀性水泥灰浆的限制膨胀标准试验方法 | | 2. | The experiment , results revealed that crack - resistant and water - repellent concrete prepared on those proportion had a good restricted expansion coefficient and high impermeability
通过试验研究，据此而配制的防水抗裂混凝土具有较好的限制膨胀率和抗渗性能。 | | 3. | This provides the probability to design the expansive concrete with different expansive energy levels and different strength grades . if blast furnace slag ( bfs ) or fly ash ( fa ) is added , e2 will decrease
在hpec砂浆中掺入磨细矿渣( bfs )或粉煤灰( fa ) ，试件限制膨胀率有所下降， csa掺量越高，掺bfs或fa后限制膨胀率下降幅度越大。 | | 4. | The more the csa , the larger the reducing percentage of e2 when adding bfs or fa . so to rema in the e2 unchanged , csa dosage should increase properly . when csa dosage is very large , adding bfs or fa will restrain possible structure destroy which is caused by excess expansion
所以体系中掺加bfs或fa后要保持限制膨胀率不变，应适当提高csa的掺量；而当csa掺量过大时， bfs或fa的掺入可抑制由于过度膨胀所造成的结构破坏。 | | 5. | After bfs is put into high strength superplasticized expansive concrete ( substituted for cement ) , autogenous shrinkage does n ' t appear in 1 day standard curing , and e2 in 14 day ' s age is higher than that of high strength superplasticized expansive concrete without bfs in the same age
高强流态膨胀混凝土掺入磨细矿渣(等量替代水泥)后，标准养护1天未出现自收缩， 14天的限制膨胀率明显高于未掺磨细矿渣的高强流态膨胀混凝土的对应值。 | | 6. | The expansion and strength of middle strength superplasticized expansive concrete develop more coordinately . fa reduces the early strength of middle strength superplasticized expansive concrete , and this make more expansion become invalid when the concrete is in plastic state
中强流态膨胀混凝土的膨胀与强度性能发展比较协调，粉煤灰的加入降低了早期强度，使更多的膨胀变为无效膨胀消耗在仍处于塑性状态的混凝土中，混凝土限制膨胀率减小。 | | 7. | The result shows that , when expansion agent is added , shrinkage can he compensated at some extent and crack can be restrained or reduced effectie1y and then the concrete ageing resistance can he enhanced , and under experiment condition , the appropriate mix content of the expansion agent should be less than 6 % , finally , for compensation shrinkage concrete , the restrictive expansion rete should he the primary index
结果表明，加入膨胀剂能补偿部分收缩，有效抑制或减少裂缝的产生，提高混凝土的耐久性；试验条件下试验所用膨胀剂的适宜掺量应小于6 % ；对补偿收缩混凝土，其限制膨胀率应作为第一性指标。 | | 8. | From the research on hpec we can know that expansion property of high strength superplasticized expansive concrete shows obvious particularity compared with ordinary expansive concrete . when bfs is not put in , high strength superplasticized expansive concrete shows autogenous shrinkage in 1 day standard curing . and in 14 day ' s age e2 is less than half of middle strength superplasticized expansive concrete ' s with same csa dosage , and this shows expansion effect is confined more
对hpec混凝土的研究发现，与普通膨胀混凝土相比，高强流态膨胀混凝土的膨胀性能表现出明显的特殊性，在不掺超细矿物质掺合料(磨细矿渣)时，高强流态膨胀混凝土标准养护1天时出现自收缩， 14天时其限制膨胀率不到相同csa掺量的中强流态膨胀混凝土限制膨胀率的一半，表现为膨胀效应受到更大限制。 | | 9. | The study on hpec mortar shows that restricted expansive ratio ( e2 ) increases in the curve of parabola with the increase of the dosage of calcium sulphoaluminate ( csa ) expansive agent . so there is a suitable range of csa dosage ( generally 6 % - 12 % ) . in this range , e2 of hpec mortar can reach as high as ( 5 - 10 ) 10 ~ 4 , and the strength is not decreased
对hpec砂浆的研究表明，限制膨胀率随膨胀剂csa掺量的增加呈抛物线形式递增，存在一个合适的csa掺量范围(一般为6 - 12 ) ，在该范围内hpec砂浆限制膨胀率可高达5万- 10万，且保证强度不下降，这就为设计不同膨胀能级膨胀混凝土而又保证混凝土强度等级提供了空间。 |