| 1. | Study on bromo - epoxy resin cured by novolac resins
酚类固化剂固化体系的研究 |
| 2. | Adsorption and decolourization of amino - novolac resin for dyes wastewater
胺基酚醛型吸附树脂对染料废水的吸附与脱色 |
| 3. | Application of glass flakes in novolac - epoxy vinyl ester resin anticorrosive coatings
玻璃鳞片在酚醛环氧乙烯基酯树脂防腐涂料中的应用 |
| 4. | The thermal stability of novolac resin / clay nanocomposites was improved when compared with pure novolac resin
剥离型的酚醛树脂纳米复合材料热稳定性得到了一定程度的提高。 |
| 5. | For phenolic resin / clay system , the intercalation and exfoliation of organoclay in phenolic and novolac resin were also investigated
对于酚醛/粘土复合体系，研究了粘土在酚醛树脂中插层和剥离行为。 |
| 6. | However , phenolic plastic ( novolac ) prepared with two - step method is mostly cured with htma and this curing process will release ammonia from htma , which will corrode the copper or brass parts
然而两步法生产酚醛塑料要加入固化剂六亚甲基四胺( htma ) ，而htma分解，残留在塑料制品中的游离氨会腐蚀电器的金属部分。 |
| 7. | Exfoliated novolac resin / clay nanocomposites can be prepared when such composites were cured in the presence of ethanol , which was employed as solvent . the influence of solvent on the microstructure of novolac resin / clay composites iii was studied
本文采用溶液聚合的方法制备了剥离型热塑性酚醛树脂/蒙脱土纳米复合材料，并且就溶剂对层状蒙脱土的插层和剥离的影响进行了研究。 |
| 8. | It is suggested that the introduction of ethanol as solvent not only decrease the viscosity of composites allowing the easy mass transfer of resin and curing agent during curing , but also weakens the intermolecular interaction of novolac resin resulting better miscibility of resin and clay
研究表明，乙醇的加入可以减小体系的级度，利于酚醛树脂和固化剂扩散到粘土层间；同时又减弱了酚醛树脂自身的相互作用，改善了酚醛和粘土的相容性。 |
| 9. | The results indicate that good mechanical properties are obtained under condition that the content of dk3 is 3wt % in resin , resin is consisted of the ratio of 3 : 7 ( novolac : resol ) and proportion of resin with reinforcer is 35 / 65
结果表明，当树脂含量为35 ，树脂中novalac含量为30时，样品的力学性能最好。在此条件下，采用dk1的复合材料的力学性能增加不明显，而采用dk3的复合材料的弯曲强度和冲击强度分别比未采用dk3的增加了34和25 。 |