| 1. | There is a complementary divergence of views of the structure of amorphous polymers .
关于无定型聚合物结构有着互补的分歧意见。 |
| 2. | After coating on the surface of silica , gd2o3 : eu has better luminescence properties
包覆后使sio2从无定型向晶型转变的温度明显降低。 |
| 3. | By means of x - ray diffractometry , it is found the fluorocarbon films are amorphous
X - ray衍射仪对溅射沉积膜的结构进行了研究结果表明cf膜是无定型的。 |
| 4. | 5 . amorphous ruos xt ^ o was intensively used as electrode materials for pseudo capacitors
在法拉第准电容器中，目前研究最多的是无定型的rlloz ? xhzo 。 |
| 5. | The xrd results reveal that the oxides coated are non - crystal and xps results reveal that it has chemical bonder with the surface of graphite particle
Xrd分析显示包覆物以无定型态存在， xps分析表明石墨表面与包覆物产生了化学结合。 |
| 6. | Specility : lt is white or near ly white unshaped power . lt has no odour , little sweet . lt can be dissolved in boiled waterand indissolved in ethano or aether
特征：白色或类白色的无定型粉末；无臭、味微天甜，在沸水中易溶解，在乙醇或乙醚中不容。 |
| 7. | First , the solid ice on the surface could have been annealed , meaning that its temperature could have been raised above the 78 kelvin mark to allow the amorphous ice to recrystallize
首先，表面的固体冰曾经退火过，也就是说其温度曾升高至78k以上使无定型冰重新结晶。 |
| 8. | The paper presents the chemical function of zeolite 4a , the silicate , the amorphous silicate , the layered silicate of green phosphorus detergent and its present development
摘要概述了绿色洗涤剂助剂4a沸石、硅酸盐、无定型硅酸盐、层状硅酸盐等化学性能，研究现状，以及它们的进展。 |
| 9. | The former electrode is manufactured in two steps . first , amorphous hydrated ruo _ 2 power is made from stuff rucl _ 3 ? nh _ 2o in colloidal way . then the power is mixed with adhesive and conductive agent , coated on ta foil by heat - press
粘合剂法制备电极片分为两步,首先以水合三氯化钌为原料用胶体法制备出无定型水合氧化粉体,然后将粉体加粘合剂和导电剂压制到基体钽箔上。 |
| 10. | The molecular structure of the sputtered titanium oxide films were investigated by xps and x - ray diffraction . it was found that the ratio of ti / o increases when pressure increases , and there is a optimum ratio of ar / o2 for the sake of obtaining more tio2 on pet surface
利用x射线衍射法( x - ray )对溅射沉积膜的表面物相结构进行了研究，发现在本实验室条件下溅射生成的膜均是无定型结构。 |