Chinese translation for "焙烧时间"

roasting time

Related Translations:

焙烧:  roast; bake; torrefy; calcination; torrefaction◇焙烧料 calcines; 焙烧炉 roaster; roasting furnace; 焙烧窑 burning-in kiln

完全焙烧:  complete roastingdead roastingultimate roasting

焙烧强度:  fired strengthintensity of roasting

焙烧条件:  firing condition

脱硫焙烧:  desulphurizing roasting

炉渣焙烧:  slag roasting

焙烧鼓风炉:  roasting blast furnaceroasting blastfurnace

焙烧不足:  insufficient firingunderroasting

焙烧窑:  burning kilnburning-in kilncalcinercalcining kilnroasting kilnstack kiln

烧结焙烧:  agglomeration roastingsinter returns roastingsinter roasting

Example Sentences:

	1.	It ' s obtained that ph = 6 . 5 is a suited ph value for getting ideal product with good properties . the calcinate temperature is the key factors to transform the precursor to a pure product with spinel structure 研究了不同的工艺条件如溶液ph值、焙烧温度、焙烧时间、焙烧方式、 li / mn的比值对产物结构的影响。
	2.	Spinel limn2o4 begin to form at 350 with the sintering time of 4 hours because there are one li + and two mn2 + in one precursor molecule . when the sintering temperature is larger than 750 , a specific sintering route is designed to avoid the formation of li2mno3 impurities 前驱体的焙烧温度和焙烧时间对limn _ 2o _ 4样品的晶相结构有很大的影响，焙烧温度高于750时，应采用分段焙烧工艺以防止局部高温形成li _ 2mno _ 3杂质。
	3.	Through the synthesis of licoo2 by using non - water dispersant and two - step roasting , influences of microstructures of precursor , the roasting temperature and the reaction time on the electrochemical properties of licoo2 were studied . it indicated that co3o4 with nano - crystalline have very good electrochemical property , and can shorten solid reaction time 02的制备工艺，考察了不同微结构的co30 ;先驱物，焙烧温度和焙烧时间等工艺条件对licoo ，电化学性能的影响，其中以纳米晶co3o ;制备出的licooz表现出优良电化学性能，且大大缩短了反应时间。
	4.	The characteristic of different products at different calcinating temperatures and time , ph value of solution , raw materials were investigated . the results show that perfect spinel li4mn5o12 crystals whose size belongs to nanometer can be obtained from the precursor of lithium manganese oxides after being calcinated . it is founded that calcinating temperature has great influence on the crystal structure of li4mn5o12 and the optimized temperature is 500 结果表明焙烧温度是影响产物结构性能的最重要的因素，最佳焙烧温度为500 ，温度小于200不能形成完整的尖晶石结构，而焙烧温度超过500产物会发生分解；综合考虑焙烧时间最佳为8小时；溶液ph值也是影响产物性能的因素之一，实验证明前驱体合成ph = 9 . 0最佳；另外不同的原料也会影响产物的结构，考察了不同锂源的影响，选择li _ 2co _ 3为最佳锂源。
	5.	( 2 ) the affecting factors such as components in precipitation process , the add - on , add on of precipitator , calination temperature and calination time were studied in the preparation process of ceo2 nanoparticles . the tg was used to analyze the processor , the xrd , sem and tem were used to characterize the size of crystal type of products . by a series of designed experiments the interaction between different factors and impacts on the preparation of ceo2 nanoparticles were probed , and the optimum preparation condition was gotten ( 2 )对纳米二氧化铈制备过程中可能的一些影响因素(反应组分的浓度，沉淀剂的加入量，焙烧温度，焙烧时间等)进行了研究，并通过tg ? dta分析手段对前驱物进行热重分析；用xrd 、 sem及tem等测试手段对产物的粒度和晶型进行分析；探索了各个因素对纳米二氧化铈制备的影响及各因素间的交互作用；确定了在该试验条件下制备纳米二氧化铈比较优化的制备条件。

Similar Words：

"焙烧热" Chinese translation, "焙烧熔炼" Chinese translation, "焙烧砂型" Chinese translation, "焙烧蛇纹石" Chinese translation, "焙烧设备" Chinese translation, "焙烧室" Chinese translation, "焙烧试验" Chinese translation, "焙烧收缩" Chinese translation, "焙烧竖炉" Chinese translation, "焙烧苏打灰" Chinese translation