Chinese translation for "硫化温度"
|
- cure temperature
curing temperature
Related Translations:
硫化钴: cobalt sulfidecobaltous sulfide 硫化铝: aluminium sulfidealuminium sulphide 硫化罐: curercuring autoclavecuring ovencuring pan boilerheatervulcanizervulcanizing boilervulcanizing tank
- Example Sentences:
| 1. | Higher sulfidation temperatures can results in coarser fes2 grains , higher electrical resistivity and higher possibility to produce p - type thin films
硫化温度越高， fes2晶粒尺寸越大，薄膜电阻率越高，并趋于p型导电。 | | 2. | In theory , the sns thin films can also be prepared in the sulphurisation temperature being 280 ~ 290 and the sulphurisation time being 20 ~ 40 minutes
在理论上,硫化温度为280 ~ 290硫化时间为20 ~ 40分钟时也能制备sns薄膜。 | | 3. | Expatiation is on made the mechanism of rubber foaming process , and the effect of types of foaming agent , dosage of foaming agent temperature of sulfuration on rubber foaming process
摘要通过试验，探讨了橡胶的发泡机理及发泡剂种类、发泡剂用量、硫化温度对橡胶发泡的影响。 | | 4. | The results indicate that the reaction temperature to form fes _ 2 fully is 400 ? . higher temperature than 400 ? makes an insignificant acceleration to the conversion from fe to fes2
研究结果表明，硫化温度为400时能充分形成fes _ 2 ，高于400后，硫化温度的升高对fes _ 2的形成没有明显的促进作用。 | | 5. | The effects of the sulfidation parameters on the microstructure and photoelectrical characteristics of fes _ 2 thin films have been investigated by the sulfidation annealing for the fe films under different temperature , time and pressure
本文采用不同的硫化温度、时间和压力对相同厚度的fe膜进行硫化处理来研究硫化参数对薄膜组织和光电性能的影响。 | | 6. | By analyzing the structures and optical and electrical properties of the sns thin films , the optimum technique parameters of preparing sns films have been obtained : the sulphurisation temperature being 200 ~ 220 and the sulphurisation time being 60 ~ 90 minute
研究了工艺参数对所制备的sns薄膜的影响规律,初步探索出制备sns薄膜的最佳工艺参数:硫化温度为200 ~ 220硫化时间为60 ~ 90分钟。 | | 7. | When sulphurisation time is 30 minutes and sulphurisation temperature change from 180 to 240 , the atomic ratio s / sn of the films increases from 0 . 72 to 1 . 08 and energy gap of the films increases from 1 . 44ev to 1 . 48ev with the increasing of the sulphurisation temperature
当硫化时间为30分钟硫化温度在240 ~ 310之间变化时,薄膜的s / sn值随着硫化温度的升高从1 . 08上升到1 . 96 ,能带间隙随着硫化温度的升高从1 . 01ev上升到1 . 72ev 。 | | 8. | Making sensitive material : made in non - sulfur vulcanization system with the formula : epdm 100kg , dicumylperoxide ( dcp ) 2kg as cross - linking agent , stearic acid 1kg as processing aid , oxidized zinc ( zno ) 3kg as accelerant , wax oil 10kg as lubricant ; and made in vulcanizing condition : vulcanizing temperature 170 c , vulcanizing time 15minutes , vulcanizing pressure 3 mpa , the vulcanized epdm is optimal sensitive material for petrol . the sensing head equipped with the vulcanized rubber possesses two qualities : better swelling response and better anti - interfere against temperature variation
敏感材料的制备：用无硫硫化体系；配方为：生胶100kg ， dcp2kg ，硬脂酸1kg ， zno3kg ，石蜡油10kg ；硫化条件：硫化温度170 ，硫化时间15分钟，硫化压力3mpa ，制备的硫化橡胶对汽油的监测较理想，用其装备的传感头不仅有较好的溶胀响应性能，而且有很好的抗温变干扰能力。 |
- Similar Words：
- "硫化铜钒矿" Chinese translation, "硫化铜整流" Chinese translation, "硫化铜整流器" Chinese translation, "硫化烷基" Chinese translation, "硫化烷基胂" Chinese translation, "硫化钨" Chinese translation, "硫化钨硬质合金金相样品的制备" Chinese translation, "硫化物" Chinese translation, "硫化物；硫醚；硫化" Chinese translation, "硫化物冰铜" Chinese translation
|
|
|