| 1. | The degree of crystallinity can be increased by annealing in an inert atmosphere .
结晶度可通过在惰性气体中的退火处理来提高。 |
| 2. | The crystallinity of azo thin films became better after annealing treatment
退火处理能使其结晶度提高。 |
| 3. | Effects of annealing treatment on physical properties of a dental all - ceramic system
退火处理对牙科全瓷冠物性的影响 |
| 4. | Effect of the structures of iron - passived porous silicon annealed in pure nitrogen ambients
高纯氮气退火处理对铁钝化多孔硅形貌的影响 |
| 5. | One diffraction peak of the secondary phase was found in the xrd spectrum of sample annealing at 850 for 15s
在850 + 15s退火处理的样品中发现了第二相形成的衍射峰。 |
| 6. | 3 . the luminescence intensity of annealed nanoparticles was compared with that of the commercial bulk powders
3系统的比较了退火处理后zns纳米晶和商用荧光粉的光致发光强度。 |
| 7. | But long time anneal will cause thermal degradation the whole spin - valve because of interlayer diffusion
但长时间的高温退火处理将会造成自旋阀其它各层之间的界面扩散，影响其性能。 |
| 8. | In this paper , the effect of heat treatment on the magnetic properties of s s fibers was studied
对不锈钢纤维进行退火处理，以探索材料成分、热处理工艺与相结构和纤维磁性能的关系。 |
| 9. | Explanation carries out annealing handling for sample , the coercivity of pellet membrane average , it is little to reduce
5910e之间。说明对样品进行退火处理，颗粒膜的矫顽力平均来说减小了。 |
| 10. | It was reported that the secondary phase of mnas has been found in gaas substrate by mn - implanted and subsequent rapid thermal annealing
有报道称采用离子注入的方法将mn ~ +注入到gaas单晶衬底中，经过快速热退火处理后，发现在晶体中生成了mnas第二相。 |