Chinese translation for "compatilizer"

相容剂

Example Sentences:

	1.	( 2 ) when the content of organobentonite was 3wt % , the intercalation behaviors depended on the chain length of organic modifier in the bentonite and the content of compatilizer （ 2 ）在有机膨润土含量为3wt %时，插层的效果决定于有机改性剂烷基链的长度和相容剂的用量。
	2.	The mechanical tests result showed that when the mmt content is 2 % and the compatilizer content is 15 % , the pmc has best mechanical property . the izod impact strength is 16 . 45 kj / m2 and the tensile strength is 35 . 77 mpa , increasing 280 % and 4 . 3 % , compared with pure pp . the pom photo indicated that the o - mmt can reduce the scale of spherical crystal of pp 以am为插层剂得到的聚丙烯蒙脱土纳米复合材料中，蒙脱土保持剥离状态，但力学性能不理想，当土含量为0 . 5时，材料的冲击强度为9 . 58kj m ~ 2 ，拉伸强度为25 . 5mpa 。
	3.	The result showed that ( 1 ) organic modifier can reduce the polarity of na - bentonite , and compatilizer ( maleic anhydride grafted polyethylene ) can strengthen the polarity of polyethylene and the interface compatibility between polyethylene and bentonite . when the number of methylene groups in alkylamine was larger than 16 , the intercalation nanocomposites were obtained 研究结果表明， （ 1 ）有机改性剂能够降低钠基膨润土的极性，相容剂（马来酸酐接枝聚乙烯）对增强聚乙烯的极性，增强聚乙烯和膨润土的界面相容性有很大作用。
	4.	Nonpolar polypropylene has bad compatibility with mmt even after organic modification to mmt . so polypropylene ( pp ) grafting acrylic acid was produced by the suspension grafting method as compatilizer . as pp / mmt nanocomposites prepared from htab modified mmt as concerned , the interlayer spacing of mmt is 4 . 61nm , 4 . 2nm and 4 . 09nm respectively when the mmt content is 1 % , 2 % and 3 % . so , the abtained nanocomposites has intercalated structure 当土含量为2 ，相容剂用量为15时力学性能最好，缺口冲击强度和拉伸强度分别达到16 . 45kj m ~ 2和35 . 77mpa ，分别比纯pp增加了280和4 . 3 ，蒙脱土的加入起到了增韧和增强的双重作用。
	5.	( 3 ) when the content of compatilizer were 15wt % 30wt % ( to high density polyethylene ) , the intercalation high density polyethylene / bentonite nanocomposites were obtained . ( 4 ) the intercalation nanocomposites were obtained after bentonite compounded with low density polyethylene and liner low density polyethylene respectively （ 3 ）当相容剂含量为15wt % 30wt % （对于高密度聚乙烯） ，能够得到插层型高密度聚乙烯/膨润土纳米复合材料。 （ 4 ）低密度聚乙烯和线型低密度聚乙烯与膨润土复合后也能够分别获得插层型纳米复合材料。

Similar Words：

"compatiblity" Chinese translation, "compatiblizing agent" Chinese translation, "compatiblizing technology" Chinese translation, "compatibly" Chinese translation, "compatiibilization" Chinese translation, "compatriot" Chinese translation, "compatriot party" Chinese translation, "compatriots in hong kong and macao" Chinese translation, "compatriots in taiwan" Chinese translation, "compay computer payroll" Chinese translation